胶条式中空玻璃的组装对工艺的要求相比铝条式中空玻璃的组装对环境和湿度的要求是不一样的。

The assembly of rubber strip insulated glass requires different processes compared to the assembly of aluminum strip insulated glass, which requires different environmental and humidity requirements.

胶条式中空玻璃组装对环境的要求：胶条式中空玻璃加工温度冬季应在10-20度之间，夏季应在20-30度之间为宜。

The environmental requirements for the assembly of rubber strip insulated glass: The processing temperature of rubber strip insulated glass should be between 10-20 degrees Celsius in winter and 20-30 degrees Celsius in summer.

胶条式中空玻璃组装相对湿度的要求：因胶条式中空玻璃干燥剂呈粉末状，与胶混合均匀后干燥剂发挥作用较慢，所以应保证胶条装配区域相对湿度稍低。

Requirements for relative humidity in the assembly of rubber strip insulated glass: As the drying agent for rubber strip insulated glass is in powder form and mixed evenly with the adhesive, the drying agent will have a slower effect. Therefore, it is necessary to ensure that the relative humidity in the assembly area of the rubber strip is slightly lower.

铝条式中空玻璃组装在温度上要求更高一些，相对湿度要求也更严格。

Aluminum strip insulated glass assembly requires higher temperature and stricter relative humidity requirements.

铝条式中空玻璃组装对环境的要求：温度也应在10-30度之间

Environmental requirements for the assembly of aluminum strip insulated glass: the temperature should also be between 10-30 degrees Celsius

铝条式中空玻璃组装相对湿度的要求：此种中空玻璃对相对湿度的要求稍低一些，正常情况即可。但应注意的是，干燥剂应选择正规厂家的合格产品，以保证干燥剂的有效使用。干燥剂开封后好于二十四小时之内用完，因为聚硫胶的透气性较大，密封性差，因此要采用双道密封。用丁基胶作为第一道密封，起到阴隔气体的作用。用聚硫胶作为第二道密封，主要作用是粘结作用，其次才是隔气作用。实践证明，单产密封的中空玻璃寿命只有5年左右，而双道密封的中空玻璃寿命可长达20年甚至40年以上，因此，发展双道密封中空玻璃是大势所趋。

Requirements for relative humidity of aluminum strip insulated glass assembly: This type of insulated glass has slightly lower requirements for relative humidity, which is sufficient under normal circumstances. However, it should be noted that desiccants should be selected from qualified products from reputable manufacturers to ensure their effective use. It is better to use the desiccant within 24 hours after opening, because the polysulfide adhesive has high breathability and poor sealing performance, so a dual seal is required. Using butyl rubber as the first seal serves as a barrier for gas separation. Using polysulfide adhesive as the second sealing layer mainly serves as a bonding effect, followed by a gas barrier effect. Practice has proven that the lifespan of single sealed insulating glass is only about 5 years, while the lifespan of double sealed insulating glass can reach 20 years or even more than 40 years. Therefore, the development of double sealed insulating glass is the trend.